下面列出擠出的是Xtel XE系列化合物(Xtel PPS)擠出工藝指南
• 28:1 to 32:1 L/D
• General Purpose screw with 2.5:1 to 3:1
Compression ratio. Mixing head optional.
• 20/60/100 Screen-pack
• Rupture disk
• Heated die clamp
Melt Pump
• Melt pumps are beneficial for producing
the most consistent and uniform sheet,
but are not required for processing Xtel XE Series compounds(Xtel PPS)
Sheet Die
• Die head suitable for low viscosity, high
temperature materials
烘干溫度
• 275°F to 300°F (135°C to 150°C)至少4個小時
• Hopper driers and/or desiccant driers are
not required
Temperature Profile for 3:1 Screw
Extruder Zone 1 550°F (288°C)
Extruder Zone 2 570°F (300°C)
Extruder Zone 3 570°F (300°C)
Extruder Zone 4 570°F (300°C)
Extruder Zone 5 570°F (300°C)
Adaptor 570°F (300°C)
Die 1 560°F (293°C)
Die 2 560°F (293°C)
Die 3 560°F (293°C)
*Lowering the temperatures after startup may
help with finish quality.
Roll Stack Temperature Profile
Roll #1 260°F (126°C)
Roll #2 275°F (135°C)
Roll #3 290°F (143°C)
加工注意事項:
Xtel PPS需要足夠的加熱時間,啟動擠出機至關重要的是確保穩定加工的溫度。如果溫度不夠擠出將造成的阻塞。 Xtel XE系列化合物(Xtel PPS)過程更擠出率較高的地方是從螺桿融化而不是加熱器。擠出機應調整到高于50%的過程中運行的溫度,同時盡量減少停留時間。皂泡,煙霧或凝膠都是在擠出機里過于熱,時間太久而造成的。溫度適當調整,但模具不低于540華氏度(282℃)設置。如果需要熔體溫度降低,選的調整擠出機的溫度分布,而不是降低模具溫度。持續融化以上600 °F對于長期的時間段(315℃)的溫度會導致材料熱降解的結果。
清洗程序:加工設備Xtel XE版系列化合物(Xtel PPS)的傳輸速率較佳處理用分數熔體流動高密度聚乙烯(Marlex HHM 50100)來清洗。料桶和螺釘應該清洗潔凈。
如有疑問可繼續瀏覽更多Xtel PPS加工指南或聯絡我公司客戶服務中心索取該資料.
"Xtel PPS板材擠出工藝指南"由“工程塑料公司”-深圳易欣園塑料化工整理發布,如需轉載請注明來源及出處,原文地址:http://m.ljwcyy.com/baike/Xtel_PPSBanCaiJiChuGongYiZhiNan/
深圳市易欣園塑料化工有限公司是過去8年間與客戶一起成長過來的易明塑膠原料。現正式更名為深圳市易欣園塑料化工有限公司,從而發展成高尖的塑化公司,長期經營PC工程塑料、ABS工程塑料、ASA塑膠原料、PVC塑膠原料、PET工程塑料等材料。公司的核心業務是開發、生產和銷售塑料、橡膠、特殊化學品和化學中間體產品。此外,易欣園還幫助客戶開發、實施定制的系統解決方案。
深圳市易欣園塑料化工有限公司
電話:+86 0755-21385289
手機:13790212223(雷先生)
手機:13790392935(易小姐)
地址:深圳市光明新區公明街道合水口新村一排一巷5055號信天大廈704